LAMI-TACK - Specification and Physical Properties
Specification of LAMI-TACK
| Grade | Base film | Both treatment type | Lamination side | Application | ||
|---|---|---|---|---|---|---|
| SSO | OPP |  |
Innner side | Print lamination(Gloss type) | ||
| MSSO | Matte OPP | |
Innner side | Print lamination(Matte type) | ||
- Standard length
SSO: 3000m
SSO: 2750m - We can also produce other type of base film Lami-Tack as desired.
Physical properties of LAMI-TACK gloss type
| Properties | Unit | LAMI-TACK | Solvent - type lamination |
Test method | |||
|---|---|---|---|---|---|---|---|
| SSO | MSSO | ||||||
| Both treatment type | |||||||
| Wetting tension | Base film side | mN/m | 38 | 39 | JIS K-6768 | ||
| Gloss after lamination | Base film side | % | 88.4 | 5.0 | 79.0 | JIS K-7105 | |
| Adhesive strength |
100°C | immediately after |
6.9 (700) |
7.1 (710) |
immediately after 2.2 (220) 3 days after 3.5 (340) |
- | |
| 3 days after | 11.7 (1190) |
11.2 (1120) | |||||
| 110°C | immediately after |
N/25mm | 9.5 (970) |
8.4 (850) |
|||
| 3 days after | (g/25mm) | 12.3 (1250) |
11.0 (1130) | ||||
| 120°C | immediately after |
9.8 (1000) |
9.2 (930) |
||||
| 3 days after | 12.5 (1270) |
11.6 (1190) |
|||||
| Appearance | |
- |  |
JF Method | |||
- Measuring condition (Room thmperature: 23°C, Humidity: 50%)
- Above table contains measured values and not guaranteed values.
- Laminating conditions
Nip roll temperature: 100°C - 120°C, Line speed: 30m/min, Nip pressure: 55.6kg/cm - Test Paper
Paper: Coated paper (209.4 g/m2), Ink: TK HY-Unity Ink MZ - Measuring condition
Adhesive strength: (180° peal, 300m/min), Gloss: measuring angle60° - Appearance test
(very good) 
(good) (not good) 
(bad)